Introduction
FLH211、FLH311、FLH310
Natural quartz ingot made by flame fusion process, less bubble, high transparency and good geometry , optimum rate of utilization.
FLH321、FLH320
High purity natural quartz ingot ,made by flame fusion process, less bubble , high transparency and good geometry , optimum rate of utilization.
FLH321H、FLH320H
High purity natural quartz ingot with lower aluminum、low alkali metal elements.
FLH321HS
Almost bubble free, ultra-high purity, low alkali and low aluminum, almost no wrapping, strong high temperature resistance, it is an ideal window material.
FLH321N、FLH320N
Norwegian sand material , made by flame fusion process, less bubble, high transparency and good geometry , optimum rate of utilization.
The material has few bubble in it with excellent transparency and geometric dimension .They are widely used for semiconductor,Optical Fiber, Solar Energy Photovoltaics, Optical Coating/Filming.
Thanks to the few bubbles, high purity, almost no inclusion, high temperature resistant performance and other characteristics,FLH321HS has been widely used in semiconductor advanced manufacturing, optical, chemical processing, UV and high temperature window.
Chemical purity
FLH211/FLH311/FLH310 Impurity Typical Value (ppm)
Al
22.00
B
0.20
Ca
1.50
Co
＜0.05
Cu
＜0.05
Fe
1.50
K
2.00
Li
2.00
Mg
0.30
Mn
＜0.10
Na
2.00
Ni
＜0.10
Ti
2.00
OH
~200
FLH321/FLH320 Impurity Typical Value (ppm)
Al
14.20
B
0.08
Ca
0.50
Co
0.50
Cu
＜0.01
Fe
0.23
K
0.30
Li
0.50
Mg
＜0.05
Mn
＜0.05
Na
0.30
Ni
＜0.05
Ti
1.30
OH
~200
FLH321H/FLH320H Impurity Typical Value (ppm)
Al
8.00
B
0.04
Ca
0.60
Co
0.05
Cu
＜0.01
Fe
0.10
K
0.20
Li
0.40
Mg
＜0.05
Mn
＜0.05
Na
0.12
Ni
＜0.05
Ti
1.40
OH
~200
FLH321N/FLH320N 雜質元素典型值 (ppm)
Al
12.00
B
0.08
Ca
0.30
Co
＜0.02
Cu
＜0.01
Fe
0.10
K
0.20
Li
0.40
Mg
＜0.05
Mn
＜0.05
Na
0.40
Ni
＜0.03
Ti
1.20
OH
~200
FLH321HS Impurity Typical Value (ppm)
Al
7.50
B
—
Ca
0.60
Co
—
Cu
＜0.01
Fe
0.20
K
0.10
Li
0.20
Mg
0.01
Mn
—
Na
0.10
Ni
—
Ti
1.30
OH
~200
Physical Property
Mechanical Properties
Density（g/cm3）
Young’s Modulus（GPa）
Poisson’s Ration
Bending Strength（MPa）
Compressive Strength（MPa）
Tensile Strength（MPa）
Torsional Strength（MPa）
Mohs Hardness
2.2
74
0.16
65
1100
50
30
6-7
Electrical Properties
Dielectric Constant （10GHz）
Loss Factor（10GHz）
Dislectric Strength(V/m)
Resistivity （20℃）
3.74
0.0002
3.7×107
1×1016
Thermal Properties
Strain Point (η=1014.5 ℃)
Annealing point (η=1013 ℃)
Softening point (η=107.8 ℃)
Thermal Conductivity(W/m·k)(20℃)
Specific Heat（20℃）(J/kg.k)
Expansion Coefficient(x10 -7/k)
α ：20℃~320 ℃
1080
1180
1700
1.4
670
5.5
Flame Fused Quartz